LASER SURFACE TREATMENTS OF IRON-BASED SUBSTRATES FOR AUTOMOTIVE APPLICATION

    لتحميل الملف من هنا
Views  222
Rating  0
 جعفر هادي عبود المياح 21/02/2018 11:02:29
تصفح هذه الورقة الالكترونية بتقنية Media To Flash Paper

In the present work laser surface alloying of low carbon steel with carbon has been investigated for automotive application. The laser used was Nd-YAG, having a wavelength of 1.06?m. It was operated at energy levels between 5 – 30 J, pulse duration from 1.5-4msec and beam diameter varied between 1-3mm. As a result of laser treatment at different energy levels and pulse durations, treated layers of varying thickness between 0.03-0.20mm with carbon concentrations exceeding the eutectic point are produced. As a consequence of this treatment, a range of microstructures and microhardness values was obtained. High hardness values were observed in the layers with predominantly martensite structure (650Hv) and relatively low values in region showing austenite microstructure (500Hv) and maximum hardness (850Hv) was found in the layer, which showed large proportion of Fe3C. Surface melting of nodular cast iron by ruby laser (0.69?m wavelength) has been also reported. The presence of retained austenite and martensite was found to be a characteristic feature in most of the treated layers.


  • وصف الــ Tags لهذا الموضوع
  • Laser, Heat treatment, low carbon steel

هذه الفقرة تنقلك الى صفحات ذات علاقة بالمقالات الاكاديمية ومنها الاوراق البحثية المقدمة من قبل اساتذة جامعة بابل وكذلك مجموعة المجلات العلمية والانسانية في الجامعة وعدد من المدنات المرفوعة من قبل مشرف موقع الكلية وهي كالاتي:

قسم المعلومات

يمكنكم التواصل مع قسم معلومات الكلية في حالة تقديم اي شكاوى من خلال الكتابة الينا,يتوجب عليك اختيار نوع الرسالة التي تود ان ترسلها لادارة الموقع :